The majority of our customers order glass microfluidic chips and flow cells with fluid connectors factory-installed. One of the standard fluid connectors that we offer is the Nanoport™ connector, fabricated by Upchurch Scientific.

on July 27, 2014

Most readers will agree that glass is a "brittle" material.  It is our everyday experience (well, hopefully you don’t really test this every day!) that glass will break abruptly, without first deforming.

on July 23, 2014

Translume has the ability to fabricate microfluidic channels of almost any shape and size that you can envision.

on July 13, 2014

Chemical Properties

Fused Silica Chemical Composition

Translume works with Fused Silica (also called fused quartz). This glass is composed exclusively of high-purity silica (SiO2) in amorphous (non-crystalline) form. In contrast, other common glasses (Pyrex, borosilicate, soda-lime, etc.) are mixed composition glasses – in addition to SiO2, they include such ingredients as Na2O, CaO, and B2O3. These additional ingredients modify the optical and mechanical characteristics of the glass and lower the melt temperature of the mix. Fused Silica, on the other hand, is pure SiO2. It has a much higher working and melting temperature than other common optical glasses, it also has exceptional optical, thermal, and mechanical properties.

Fused Silica Chemical Purity

Contaminants, despite their presence at very low levels, have subtle yet significant effects. Purity is mostly determined by the raw material, the manufacturing method and subsequent handling procedures. Special precautions must be taken at all stages of the manufacturing process to maintain high purity.

The most common impurities are metals (Al, Na and Fe among others), water (present as OH groups), and chlorine. These contaminants affect the viscosity, optical absorption and electrical properties of the glass.

Chemical Compatibility

Due to its pure composition, Fused Silica is an extremely inert glass.  It is compatible with the vast majority of chemicals used in the industry and in the laboratory. There are only a few uncommon materials that will attack it, including HF (hydrofluoric acid) and hot KOH (Potassium hydroxide).

Thermal Properties

Coefficient of Thermal Expansion (CTE)

Fused Silica has a remarkably low coefficient of thermal expansion, which varies only slightly with temperature.

Fused Silica Mean Coefficient of Thermal Expansion (Source: Präzisions Glas & Optik GmbH, Menden, Germany):

  • -   0.52 x 10-6/K over the 5°C to 35°C temperature range
  • -   0.57 x 10-6/K over the 0°C to 200°C temperature range
  • -   0.48 x 10-6/K over the -100°C to 35°C temperature range

This material characteristic imparts fused silica a high resistance to thermal shock, and makes it an excellent material for applications that require the utmost in dimensional stability over a large temperature range. For comparison, INVAR (a nickel-iron alloy), which has the lowest thermal expansion among all metals and alloys near room temperature, has a mean coefficient of thermal expansion that is more than twice that of Fused Silica (1.3 x 10-6°/K over the 20°C to 100°C temperature range).

Thermal Conductivity

Fused Silica is an excellent thermal insulator. Its thermal conductivity is only 1.38W/mºK (measured at 25ºC), which is one of the lowest for any solid. For comparison, this value is 100-fold lower than that of silicon (148W/mºK @ 25 C); and one eighth of that of INVAR (10.5 W/mºK @ 25 C).

Optical Properties

Fused Silica offers a set of optical characteristics that compare favorably with other optical materials. It is transparent from the deep ultraviolet (UV) to the mid-infrared. 

Optical Absorption

Fused Silica is transparent in the ultraviolet, visible, and near infrared.

Synthetic Fused Silica

Synthetic Fused Silica transmissionSynthetic Fused Silica transmissionUnless otherwise specified we typically work with synthetic fused silica.

Shown here is a typical transmission for a 10-mm thick synthetic Fused Silica sample. The data is uncorrected for surface reflection (Fresnel) losses.

The absorption boundary on the ultraviolet side is deep in the UV. The exact location of the absorption edge is strongly affected by the presence of impurities. Synthetic Fused Silica, which is manufactured from an extremely pure precursor, offers the highest transparency in the UV of any glasses. On the infrared side, the source of intrinsic absorption is molecular vibration. The Si-O bond has a very strong absorption peak near 8.9 µm and at 4.5 µm (overtone frequency).

Additional absorption bands are present in the near infrared. These are caused by impurities. For example, water vapor creates absorption around 1.4, 2.1, and 2.8 µ m. Synthetic-grade Fused Silica is particularly likely to display water vapor absorption in the near infrared.

 

IR-Grade Fused Silica IR grade Fused Quartz transmissionIR grade Fused Quartz transmission

In Contrast IR grade fused silica contains a lot fewer water traces and shows significantly less absorption in the infrared.  This material grade is, however, not as good in the UV.

Shown here is a typical transmission for a 10-mm thick IR-grade Fused Silica sample. The data is uncorrected for surface reflection (Fresnel) losses.

 

Index of Refraction of Fused Silica

(Source: www.mellesgriot.com)

 Index of refraction of fused silicaIndex of refraction of fused silica

Temperature Dependence of Refractive Index

The refractive indices of the glasses are not only dependent on wavelength, but also upon temperature. The dn/dT for Fused Silica is 1.1x10-5/ºC at 1064nm, near room temperature.

Electrical Properties

Fused Silica is an excellent electrical insulator well into the microwave, with a dielectric loss factor of under 0.0004 at 1 MHz. 

Mechanical Properties

Less known is the fact that Fused Silica has excellent elastic properties, making it a superior material for manufacturing micro-mechanical pieces that must flex to provide some type of motion. This is counter-intuitive: To the casual observer, glass is the personification of a breakable material, or what material scientists call a brittle material; and thus, one naturally assumes it can’t be used to manufacture dynamic MEMS. When using standard fabrication processes, such as ultrasonic drilling, lapping, or sand-blasting, this is indeed true. These processes create microscopic cracks, which lower the tensile strength of the glass and make it break easily. However, when silica glass is machined with our ultra-low stress femtoEtch process, microcrack formation is prevented, and the resulting part exhibits an exceptional elastic behavior. With this low-stress approach, one can manufacture glass MEMS (GMEMS).  

For the skeptical readers, we have a video that illustrates that fused silica glass pieces can indeed bend (without breaking!).

   

 

Density

Fused Silica is a light material. Its density is 2.202g/cm3 (To a very small degree, the density is influenced by the annealing conditions of the glass near the transformation temperature). By comparison, the density of the aluminum is approximately 2.6 g/cm3, and that of Invar is 8.1 g/cm3.

Elasticity Modulus

Fused Silica shows an almost perfect brittle-elastic behavior at temperatures lower than the transformation point. Fused Silica elasticity modulus is 73 GPa at 25ºC. By comparison, steel has a Young's Modulus of the order of 205 GPa.

Effect of Surface Flaws on Mechanical Properties

Fused Silica is extremely strong in compression, with a design compressive strength greater than 1.1 x 109 Pa. Under tension, the story is more complicated. Surface flaws can drastically reduce the inherent strength of any glass. As such, tensile properties are greatly influenced by these defects and by the manufacturing process that is used to create the desired Fused Silica object.

To date, the common practice has been to use a design tensile strength for Fused Silica with 'good' surface quality, taking into consideration both safety margin and fatigue, of 5 x 106 Pa. The Translume manufacturing process is exceptionally gentle and creates virtually no microcracks. Preliminary data confirms that when using Translume manufactured devices, a design tensile strength superior to 108 Pa can be safely assumed.

on July 10, 2014

Glass meltGlass meltGlass is a very old material, available well before the onset of the late Roman Empire. Precision machining of glass, on the other hand, is a very novel concept.

on April 26, 2014

Dedicated to provide our customers with the highest quality glass micromachining service

Translume has years of experience fabricating custom-designed parts out of fused silica glass. If you’re looking for high precision machining of fused silica, don’t look any further. We will provide you with the best glass micromachining solution, as we have done so for the past 15+ years for hundreds of extremely satisfied customers.

on February 27, 2014

At the request of some of our customers, and on a custom basis, we now offer microfluidic chips and flow cells equipped with Luer connectors made out of metal.

on November 06, 2013

MicroFluidic Chips

Flow Cells

Standard directly from our standard product section or your custom design